CuSn10

B10

CuSn10-B  CB480K

GB-CuSn10 2.1051

C90700

-

Resistant to heavy static shock, corrosion and temperatures up to 280°C, castability and machinability good.

CuSn10P

B101

CuSn11P-B  CB481K

-

-

PB1

Resistant to corrosion, abrasion and high mechanical loads, very good castability and machinability.

CuSn10Zn2

B102

-

GB-Rg10 2.1087

C90500

G1

Resistant to salt water corrosion, abrasion and pressure, very good castability and machinability.

CuSn10Pb10

B1010

CuSn10Pb10-B CB496K

GB-CuPb10Sn 2.1177

C93700

LB2

Resistant to abrasion, very good castability and machinability.

CuSn4Zn7Pb6

B476

-

-

C83800

LG1

 

Resistant to sea water, resistant to temperatures up to 225°C; very good castability and machinability.

CuSn5Zn5Pb5

B555

CuSn5Zn5Pb5-B CB491K

GB-Rg5 2,1097

C83600

LG2

CuAl10Fe

BA93

-

GB-CuAl10Fe 2,0941

C95200

AB1

For castings for welding Pb not more than 0.03%. Structure Material. Low temperature sensitivity in the range from-200°C to +200°C. Good resistance to corrosion and wear. High resistant to static load, corrosion, abrasion and elevated temperatures; very good castability. Density ~ 7.5 g/cm³.

CuAl10FeMn2

BA1032

-

-

-

-

Very resistant to static loads, corrosion, abrasion and increased temperature, very good castability

CuAl10Fe4Ni4

BA1044

CuAl10Fe5Ni5-B CB333G

GB-CuAl10Ni 2,0976

C95500 C95800

AB2

Highly resistant to static loads, corrosion, abrasion and elevated temperatures; very good castability. Construction material with high mechanical properties. Good resistance to corrosion and oxidation. Density ~ 7.5 g/cm3.

CuSi3Zn3Mn1

BK 331

-

-

-

-

Resistant to corrosion, load variables, impact and abrasion, good castability.

CuNi16Al9Zn9

-

-

-

-

-

Resistant to thermal shock . Good thermal conductivity. Very good castability and machinability. Weldable. Density ca.8, 2 g/cm³

CuZn39Pb2

MO59

-

-

-

-

Resistant to corrosion, variable load, impact and abrasion, good castability.

GB- CuZn37PbMs60

-

CuZn39Pb1Al-B CB754S

GB-CuZn37Pb 2,0342

-

DCB3

Resistant to minor dynamic loads and abrasion, castability and machinability very good. Contains lead addition, which improves the machinability. Tin is added to improve corrosion resistance. Aluminum forms a protective oxide layer that keeps the molten metal in a clean and reduces metal mould particle attacks.

GB-CuZn38AlMs63

-

-

GB-CuZn38Al 2,0601

-

DCB1

Construction material with good castability, cold ductility , resistant to atmospheric corrosion on the electrical conductivity of about 12m / (? X mm²).

CuZn40Mn3Fe1

MM55

-

-

-

-

Resistant to abrasion, moderately resistant to corrosion, cavitation and elevated temperatures up to 250°C; sufficient castability.

CuZn38Al2Mn1Fe

MA58

-

GB-CuZn34Al2 2,0602

-

-

Resistant to abrasion, moderately resistant to corrosion and cavitation and elevated temperatures up to 250oC; sufficient castability.

CuZn35Al5

-

CuZn35Mn2Al1Fe-B CB765S

GB-CuZn25Al5 2,0608

C86400

HTB1

Resistant to abrasion, corrosion and static load, very good castability and machinability. General technical castings. Good resistance to corrosion. The density of 8.6 g/cm³.

CuZn25Al5

-

CuZn25Al5Mn4Fe3-B CB762S

GB-CuZn25Al5 2,0608

-

HTB3

High resistance to stress and corrosion. Construction material with very high static load capacity.

CuZn16Si3,5

MK80

CuZn16Si4-B CB761S

GB-CuZn15Si4 2,0493

C87400

-

Resistant to salt water corrosion, abrasion and the temperature to 100^°C, weldable, good castability and machinability.