Products:
 Metals
|
|
Musisz uaktualniæ Flash Playera.
COPPER
|
Dimensions
|
Diameter
|
Type
|
Grades
|
|
WIRES
|
0.6 - 1 mm
|
spools
|
M1E
|
|
0,5 - 3mm
|
spools
|
M1E
|
|
RODS
|
|
6 - 120 mm
|
M1E,
MHY
|
|
|
6-130mm
|
M1E, MHY
|
|
15x3 - 120x10 mm
|
M1E
|
|
|
8-60mm
|
M1E, MHY
|
|
PIPES
|
|
5 - 170 mm
|
M1E,
M2R,
SF-CU,
M1R
|
|
|
5x0,8 - 35x1,5
|
Cu- DHP, SFCU, M1E
|
|
Dimensions
|
Thickness
|
Type
|
Grades
|
|
STRIPS
|
od 0,15
- 0,55 mm
|
Width:
300 - 670 mm
|
M1E,
M2G
|
|
0,1mm-3mm
|
Width:
0mm x 550mm
|
E-Cu, SF-Cu
|
|
SHEETS
|
od 0,8
- 30 mm
|
600-700 x 2000 mm
|
M1E
|
|
0,3mm- 150mm
|
300x650 - 1000x3000
|
E-Cu, SE-CU, SF-Cu
|
|
FLAT BARS
|
|
10x4 - 200x30
|
M1E
|
|
COPPER ANODES
|
|
10x200x600
|
M1R
|
|
Symbol
|
Marking in accordance with standards
|
Approximate characteristics
|
|
PN-91/H87026
|
EN 1982
|
DIN 17656
|
ASTM B30
|
BS 1400:1985
|
|
CuSn-
|
|
|
|
|
|
|
|
CuSn10
|
B10
|
|
|
C90700
|
-
|
Resistant to heavy static shock, corrosion and temperatures up to 280°C, good castability and machinability.
|
|
CuSn10P
|
B101
|
CuSn11P-B CB481K
|
-
|
-
|
PB1
|
Resistant to corrosion, abrasion and high mechanical loads, very good castability and machinability.
|
|
CuSn10Zn2
|
B102
|
-
|
GB-Rg10 2.1087
|
C90500
|
G1
|
Resistant to salt water corrosion, abrasion and pressure, very good castability and machinability.
|
|
CuSn10Pb10
|
B1010
|
CuSn10Pb10-B CB496K
|
GB-CuPb10Sn 2.1177
|
C93700
|
LB2
|
Resistant to abrasion, very good castability and machinability.
|
|
CuSn4Zn7Pb6
|
B476
|
-
|
-
|
C83800
|
LG1
|
Resistant to sea water, resistant to temperatures up to 225°C; very good castability and machinability
|
|
CuSn5Zn5Pb5
|
B555
|
CuSn5Zn5Pb5-B CB491K
|
GB-Rg5 2,1097
|
C83600
|
LG2
|
|
CuAl-
|
|
|
|
|
|
|
|
CuAl10Fe
|
BA93
|
-
|
GB-CuAl10Fe 2,0941
|
C95200
|
AB1
|
For castings for welding with no more than 0.03% Pb. Structure material. Low temperature sensitivity in the range from -200oC to +200 oC. Good resistance to corrosion and wear. Highly resistant to static load, corrosion, abrasion and elevated temperatures; very good castability. Density ~ 7.5 g/cm3.
|
|
CuAl10FeMn2
|
BA1032
|
-
|
-
|
-
|
-
|
Highly resistant to static loads, corrosion, abrasion and elevated temperatures; very good castability.
|
|
CuAl10Fe4Ni4
|
BA1044
|
CuAl10Fe5Ni5-B CB333G
|
GB-CuAl10Ni 2,0976
|
C95500 C95800
|
AB2
|
Construction material with high mechanical properties. Good resistance to corrosion and oxidation. Density ~ 7.5 g/cm3.
|
|
CuSi-
|
|
|
|
|
|
|
|
CuSi3Zn3Mn1
|
BK 331
|
-
|
-
|
-
|
-
|
Resistant to corrosion, variable load, impact and abrasion, good castability.
|
|
CuNi-
|
|
|
|
|
|
|
|
CuNi16Al9Zn9
|
-
|
-
|
-
|
-
|
-
|
Resistant to thermal shock. Good thermal conductivity. Very good castability and machinability. Weldable. Density ok. 8,2 g/cm3
|
|
CuZn-
|
|
|
|
|
|
|
|
CuZn39Pb2
|
MO59
|
-
|
-
|
-
|
-
|
Resistant to minor dynamic loads and abrasion, castability and machinability very good.
|
|
GB-CuZn37PbMs60
|
-
|
CuZn39Pb1Al-B CB754S
|
GB-CuZn37Pb 2,0342
|
-
|
DCB3
|
Contains lead addition, which improves the machinability. Tin is added to improve corrosion resistance. Aluminum oxide forms a protective layer that keeps the molten metal in a clean and reduces the attack of a material particle chill.
|
|
GB-CuZn38AlMs63
|
-
|
-
|
GB-CuZn38Al 2,0601
|
-
|
DCB1
|
Construction material with good castability, cold ductility, resistant to atmospheric corrosion with electrical conductivity of about 12m / (? X mm2).
|
|
CuZn40Mn3Fe1
|
MM55
|
-
|
-
|
-
|
-
|
Resistant to abrasion, moderately resistant to corrosion, cavitation and elevated temperatures up to 250oC; sufficient castability.
|
|
CuZn38Al2Mn1Fe
|
MA58
|
-
|
GB-CuZn34Al2 2,0602
|
-
|
-
|
Resistant to abrasion, corrosion and static load, very good castability and machinability.
|
|
CuZn35Al5
|
-
|
CuZn35Mn2Al1Fe-B CB765S
|
GB-CuZn25Al5 2,0608
|
C86400
|
HTB1
|
General technical casting. Good resistance to corrosion. The density of 8.6 g/cm3.
|
|
CuZn25Al5
|
-
|
CuZn25Al5Mn4Fe3-B CB762S
|
GB-CuZn25Al5 2,0608
|
-
|
HTB3
|
High resistance to stress and corrosion. Construction material with very high static load capacity.
|
|
|
MK80
|
CuZn16Si4-B CB761S
|
GB-CuZn15Si4 2,0493
|
C87400
|
-
|
Resistant to salt water corrosion, abrasion and the temperature to 100°C, weldable, good castability and machinability.
|
1 apart from the items listed in the table, we can execute on the client's request rate of any chemical composition
2 in the case of PN alloys as grade replacements in accordance with foreign standards, chemical composition and mechanical properties should be compared |
|
|